Hot Rolled Coils
HR Black : As cast/ ground slabs are first heated and soaked in reheating furnace, they are rolled to intermediate thickness in the roughing mill, and then to the final thickness in the tandem mill. Hot Strip Mill is also equipped with online surface inspection machine for detection of surface flaws during hot rolling of strips.
Hot rolled coils are annealed and pickled in continuous annealing-pickling lines having scale breaker, shot blasting unit, sulphuric acid, and mixed acid bath. HRAP coils have a cleaner surface and have improved mechanical properties for downstream processing. HRAP line is also equipped with online reduction for providing product in2B, No1, No4, BA & PVC finish.
Product	Max Width in mm		Thickness in mm
	Min	Max	Min	Max
Hot Rolled Coil	1000	1650	2	10
N1	1000	1650	2	10
2E	1000	1600	1.4	6.7

Cold Rolled Coils
Our cold rolling facility is equipped with all state-of-art facilities like 20-Hi-Sendzimier cold rolling mill with IMR Shifting, Mill Tilting and Shape meter advantages for higher degree of Shape & profile correction. The CR Annealing & Pickling line is on environment friendly LPG fuel with better and fastest temperature control associated with Electrolytic and Acid Pickling with very high control of pickling process. The online Skin Pass and Tension Leveling has made this line capable of producing finished 2B/2D product at par with international quality. The on-line automatic surface inspection system also provides a very high resolution surface quality. There is provision of offline Skin Pass Mills which helps to cater high luster requirements also. Other facilities include Bright Annealing units (under commissioning phase) in cracked ammonia atmosphere and Strip Grinding line to produce desired surface finishes.
Product	Width		Thickness
	Min	Max	Min	Max
CRAP	1000	1600	0.3	5
NOTE : SLITTED COILS AVAILABLE AS PER REQUEST

STAINLESS STEEL COILS

Coil Finishing: 2b, 2d, hr, cr, ba (no. 8), satin (met with plastic coated)

Size: Thickness: 0. 1 mm to 48 mm, width: 1000 mm to 2500 mm, length: 2000 mm to coil.

Grade: 304, 304l, 304h, 316, 316l, 316ln, 316ti, 309, 310s, 317l, 321, 347, 409, 410, 420, 430, 446 & 202

DUPLEX STEEL COILS

Dimensions: ASTM, ASME and API

Standards: ASTM A240 / ASME SA240

Size: 1 MM TO 200 MM THK IN 1000 MM TO 3000 MM WIDTH x 2500 MM / 5000 MM / 10000 MM / COIL.

Form: Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange)

Finish: Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)

Hardness : Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc.

Specialize : Shim Sheet, Perforated Sheet, B. Q. Profile.

CHEMICAL COMPOSITION
GRADE	CHEMICAL COMPOSITION	MECHANICAL PROPERTIES
302	CHROMIUM (Cr): 17-19	Ultimate Tensile Strength psi – 100,000
	NICKEL (N): 8-10	0.2% Offset Yield Strength psi – 40,000
	MAGANESE (Mn): 2.00 max	Percent Elongation in 2 inches – 50
	CARBON (C): 0.15 max	Hardness Rockwell – B85
	SULFUR (S): 0.030 max
	PHOSPHORUS (P): 0.045 max
	SILICON (Si): 1.00 max
304	Cr – 18-20	Ultimate Tensile Strength psi – 95,000
	Ni – 8-10.50	0.2% Offset Yield Strength psi – 40,000
	Mn – 2.00 max	Percent Elongation in 2 inches – 50
	C – 0.08 max	Hardness Rockwell – B80
	S – 0.030 max
	Si – 1.00 max
	P – 0.045 max
304L	Cr – 18-20	Ultimate Tensile Strength psi – 90,000
	Ni – 8-12	0.2% Offset Yield Strength psi – 40,000
	Mn – 2.00 max	Percent Elongation in 2 inches – 50
	C – 0.03 max	Hardness Rockwell – B80
	S – 0.030- max
	Si – 1.00 max
	P – 0.045 max
316	Cr – 16-18	Ultimate Tensile Strength psi – 90,000
	Ni – 10-14	0.2% Offset Yield Strength psi – 40,000
	Mo – 2-3	Percent Elongation in 2 inches – 50
	Mn – 2.00 max	Hardness Rockwell – B80
	C – 0.08 max
	S – 0.030 max
	Si – 1.00 max
	P – 0.045 max
316L	Cr – 16-18	Ultimate Tensile Strength psi – 90,000
	Ni – 10-14	0.2% Offset Yield Strength psi – 40,000
	Mo – 2-3	Percent Elongation in 2 inches – 50
	Mn – 2.00 max	Hardness Rockwell – B80
	C – 0.03 max
	S – 0.030 max
	Si – 1.00 max
	P – 0.045 max

---